For product technical information, pricing and availability contact our sales department at:
(219) 548-3799
sales@allianceorg.com
BCN - Bonded Compression Neo
BCNF - Bonded Neo Ferrite Hybrid
BIF - Bonded Injection Ferrite
BIN - Bonded Injection Neo
BIS - Bonded Injection SmCo
N - Sintered NdFeB
C - Sintered SrFe2O3 Ferrites
S - Sintered SmCo5, Sm2Co17
A - Cast and Sintered AlNiCo
(219) 548-3799
sales@allianceorg.com
BCN - Bonded Compression Neo
BCNF - Bonded Neo Ferrite Hybrid
BIF - Bonded Injection Ferrite
BIN - Bonded Injection Neo
BIS - Bonded Injection SmCo
N - Sintered NdFeB
C - Sintered SrFe2O3 Ferrites
S - Sintered SmCo5, Sm2Co17
A - Cast and Sintered AlNiCo
Ferrite C-8
«« Back to Ceramic Magnetic Materials
| Max | Min |
| Residual Induction Br | G | 4,100 | 3,900 |
| Coercive Force Hc | Oe | 3,400 | 3,000 |
| Intrinsic Coercive Force Hci | Oe | 3,450 | 3,050 |
| Max. Energy Product (BH)max | MGOe | 3.8 | 3.4 |
| Material Density | g/cm3 | 4.8 | |
| Max. Operating Temperature | C | 350 | |
| Temperature Coefficient for B | %/C | -0.20 | |
| Temperature Coefficient for H | %/C | 0.35 | |
| Required Magnetizing Force | Oe | 20,000 | |
| Material Composition | SrO-6Fe2O3 | ||
Ferrite magnets, also known as Ceramics, are the most widely used magnetic materials. Made primarily of Strontium and Iron Oxide, they are the least expensive magnets today. C-8 grade is usually
used in PMDC motor
applications.